Antas-169 Sealant Struktur Silikon

Packaging : 300mL, 590mL


antas-169 is one-component, neutral curing silicone structural sealant. It is specially designed for structural glazing in glass curtain wall, seams between structural insulated panels (SIPs). It has high performance of structural bonding and excellent weather ability. It can be widely used in broad temperature range, and is cured by the moisture in air to form an elastomeric rubber ensuring tight structural bond.
 
Product feature
1. Neutral curing, no pollution or corrosion on metal, coated glass, concrete, marble and other building materials
2. Excellent adhesion to most building materials
3. Excellent weathering performance with over 25 years’ service life under general environment.
4. Excellent performance within broad temperature range. The cured sealant will not turn brittle, hardened or cracked at -50℃. It will not turn soft or deteriorated, and will keep good strength and flexibility at 150℃.
5. Compatibility with other neutral silicone sealants and other accessory facilities of structural glazin
Main purpose
1.Structural bonding of glass curtain wall
2.Structural bonding of other curtain wall
3.Seams between structural insulated panels (SIPs)
4.Structural bonding for industrial purposes or other buildings
Standards compliant
ASTM C1184
ROSH
GB16776-2005
Technical parameters
Number Test items Standard Ordain Measured value
1 Appearance Even, exquisite paste, No bubble, no skinning, no gel Even, exquisite paste, No bubble, no skinning, no gel
2 Sag degree Horizontalmm No deformation No deformation
Verticalmm ≤3 0
3 Extrudability, s ≤10 2
4 Tack free timeh ≤ 3 1
5 Hardness, Shore A 20~60 41
6 Heat deterioration Mass loss, % ≤10 4
Crackle No crackle No crackle
Powdering No powdering No powdering
7 Tensile adhesion 23℃ Tensile strength, MPa ≥0.60 1.28
Damage area of bonding, % ≤5 0
Elongation at largest tensile strength, % ≥100 325
90℃ Tensile strength, MPa ≥0.45 0.83
Damage area of bonding, % ≤5 0
-30℃ Tensile strength, MPa ≥0.45 1.97
Damage area of bonding, % ≤5 0
After water immersion Tensile strength, MPa ≥0.45 0.93
Damage area of bonding, % ≤5 0
After water & UV-radiation Tensile strength, MPa ≥0.45 1.19
Damage area of bonding, % ≤5 0
8 Tensile modulus 23℃ Elongation is 10%, kPa --- 132.5
Elongation is 20%, kPa --- 338.0
Elongation is 40%, kPa --- 561.2
Use restrictions
antas-169 should not be applied:
1. On the surface of substrate that bleeds oil, plasticizers or solvents and so on (such as impregnated wood).
2. In totally confined spaces.
3. When substrate surface temperature beyond 40℃ or below 10℃.
4. In continuous water immersion or on the surface with fog, or wet surface, or in continuous wet place
5.On paint surface.